Abstract: Thermomechnical processing and controlled rolling of microalloyed steel sheets are affected by several factors according to the final properties of product. To create the high mechanical properties, a uniform and fine-grain structure is necessary in hot rolled final products. To produce such microstructures, every stage of the thermomechanical processing of the steel rolling has to be carefully controlled. Hence, first step is grain coarsening control that it usually occurs during reheating for slab. For this purpose, seven different reheating temperatures between 1000 to 1300 °C with 50 °C increments were chosen in this investigation for soaking treatment. By soaking the specimens in furnace, the grain coarsening temperature (Tgc) is obtained about 1250 °C. Moreover, it is observed that increasing the reheating temperatures causes more decreasing of the precipitates percentage. Hence, for these kinds of steels, the reheating temperature 1200 to 1250 °C is recommended.

Abstract: Thermo mechanical processing and controlled rolling of microalloyed steel sheets are affected by several factors. In this investigation, finishing temperature of rolling which is considered as the most effective parameters on the final mechanical properties of hot rolled products has been studied. For this purpose, three different finishing temperatures of 950, 900 and 850 °C below the non-recrystallization temperature and one temperature of 800 °C in the intercritical range were chosen. It is observed that decreasing the finishing temperature causes increase of strength and decrease of total elongation. This is accompanied by more grain refinement of microstructure and the morphology was changed from polygonal ferrite to acicular one. Findings of this research provide suitable connection among finishing temperature, microstructural features, and mechanical properties of hot rolled Nb-microalloyed steel sheets.