Papers by Author: De Liang Zhang

Abstract: TiAl alloy with a composition of Ti-43Al-5V-4Nb-Y (at.%) was prepared by spark plasma sintering (SPS). The TiAl powders were sintered between 650°C and 1300°C for 5 min under different loads. With the increasing of the temperature, the diffusion of the elements can be observed. Full compaction is achieved in a short period of time and the overall processing duration does not exceed 30 min. A fully lamellar structure was seen in the TiAl alloy after heat treatment. The microstructures of the samples were determined by X-ray diffraction and scanning electron microscopy. Their mechanical properties were evaluated by tensile tests performed at room temperature

Abstract: In this work, in-situ TiC reinforced Ti matrix composites (TMCs) have been fabricated via blending TiH₂ powder and multi-walled carbon nanotubes (CNTs) followed by thermomechanical consolidation of the TiH₂/CNTs powder mixture. The dehydrogenation, in situ reaction and consolidation occurred simultaneously and took less than 15 minutes in total. The effect of CNTs content (1 and 3 vol.% (0.56 and 1.69 wt.%)) on the evolution of microstructures and mechanical performances of the extruded samples has been investigated. The results showed that the extruded TMCs had a duplex microstructure consisting of coarse alpha titanium grains and ultrafine grained (UFG) regions, and the in-situ formed TiC particles had a near-spherical shape. The extruded sample with 1 vol.% (0.56 wt.%) CNTs reinforced exhibited a yield strength of 807.3 MPa, ultimate tensile strength of 1085.9 MPa and elongation to fracture of 3.3% at room temperature. The mechanism of microstructural evolution and material failure are discussed.e are discussed.