Papers by Author: Fa Guang Leng

Abstract: Polypropylene fiber is a new measure to prevent plastic cracks of concrete. Effects of the parameters, such as dosage and types of fibers, on the plastic cracks were studied systematically. The properties of cracking resistance of mortar, ordinary concrete and high performance concrete were investigated by using samples of two types in shape. The results show that: (1) polypropylene fibers may increase the cracking resistance of concrete further; (2) as smaller quantity of cement and higher quantity of aggregate as possible should be used to prevent concrete form cracking; (3) the main reason why polypropylene fibers increase cracking resistance of concrete is that they increase strain capacity of concrete at early age, decrease shrinkage strain, improve plastic tensile strength and decrease tensile stress of the capillary.

Abstract: The effects of Cemfiber on the workability, mechanical properties, resistance to chemical corrosion and drying shrinkage of High-Performance Concrete (HPC) have been studied systematically. The results show that: (1) the effects of Cemfiber on the workability of HPC are related to parameter of mix proportion. Generally speaking, Cemfiber does not reduce the workability of HPC; (2) the effect of Cemfiber on the compressive strength and flexural strength is very small; (3) the HPC incorporated with Cemfiber has high resistance to corrosion of hydrochloric acid; (4) Cemfiber may reduce drying shrinkage of HPC significantly; (5) Cemfiber may increase cracking resistance of HPC resulting from drying shrinkage.

Abstract: The ASTM C1202 method is observed that the total electric charge passed is not an ideal indicator for classification of concrete quality when different binders are considered. Considering the drawback of the ASTM 1202 method, a simple modification to the ASTM C1202 method is recommended. The modification involves an additional test using curing water as electrolyze solution. The difference in the total charge passed obtained between standard test and test performed in curing water is suggested as an indicator for concrete quality. The test results show that there exists a good correlation between the ACSIRO and the ASTM C1202 methods. The relationship can be formulated as a linear function.

Abstract: Based on available test data and fracture criterion, by using probability fracture mechanics and mathematical statistical method, the distribution feature of fracture toughness, IC K , of interface between coarse aggregate and hardened cement mortar is analyzed, and a method of defining the least number of specimens for testing fracture toughness is provided. Weibull distribution or lognormal distribution is often used to analyze lifetime problem, so the two models are preferentially considered. The analysis shows that the fracture toughness conforms to lognormal distribution with degree of confidence g =0.9, relative deviation d =0.05 and the least number of specimens of 13. The study results can be used in the probability fracture analysis and construction quality control of interface between coarse aggregate and hardened cement mortar.

Abstract: In this paper, the main characteristic of definition, property, requirement of raw material, mix proportion design and performance improvement of high volume fly ash concrete (for short HVFAC) are summarized. The applications of HVFAC in dam, highway, building and port are introduced. The research results have shown that HVFAC have outstanding properties of physical mechanics, but some problems need to be further studied. It is believed that an operable strict corresponding technical criterion would be set down as soon as possible for engineering practice.