Papers by Author: Feng Shi Yin

Abstract: In order to improve the corrosion resistance of sintered NdFeB magnet, experiments are done by the new process which involves ultrasonic electroforming Ni–P alloys. The influence of ultrasonic on electroforming Ni–P alloy on NdFeB was studied by using microscope, adhesion test and NaCl solution immersion test.The results showed that the Ni–P alloy deposit on NdFeB is rough and has poor adhesion without ultrasonic agitation; However, the Ni–P alloy deposit on NdFeB with ultrasonic agitation has the following advantages: uniform and smooth deposit grains, strong adhesion and good corrosion resistance.

Abstract: In this study, the machining parameters of electrical discharge machining (EDM) are varied to study the effects of electrical discharge energy on material removal rate and surface roughness of NdFeB magnet. Moreover, the micro-cracks on the machined surface induced by EDM are also examined. The experimental results reveal that the MRR increases with the electrical discharge energy. The surface cracks on the machined surface are more serious when the discharge energy is higher. Thus, using EDM process to machine sintered NdFeB magnet depends on setting the machining parameters to prevent surface crack.