Papers by Author: G. Rocha

Abstract: Composites of bovine bone derived HA with 5 wt% and 10 wt% of TiO2 were sintered at different temperatures. Their characterization comprised measurements of density, microhardness, and compression strength together with SEM observations and X-ray diffraction analysis. Better densification behaviour was achieved at higher sintering temperatures. The highest microhardness value was measured in the samples sintered at 1300°C. The best compressive strengths of the samples containing 5% and 10% TiO2 were obtained after sintering at 1300°C and 1200°C, respectively.

Abstract: Composites of calcinated bovine bone derived hydroxyapatite (HA) with 0.25, 0.5, 1, and 2 wt % La2O3 were prepared by sintering. The experimental results indicated that compression strength and microhardness of HA-La2O3 composites increase when the content of La2O3 and sintering temperature increase. The best mechanical properties were achieved after sintering at 1300°C. The results are in agreement with densification measurements and microstructure analysis.

Abstract: The properties of sintered hydroxyapatite (HA), obtained from bovine femoral shafts via calcination method, were investigated utilizing scanning electron microscopy (SEM) and X-ray diffraction analysis together with measurements of microhardness, density, and compression strength. The production of HA from natural sources is preferred due to money and time saving reasons. The results indicate the new HA materials as promissing in biomedicine, since similar mechanical behaviour was obtained with previous studies.