Papers by Author: Gabriel Vlasák

Abstract: Bilayer ribbons were prepared by rapid quenching from the melt using a double-nozzle technique. The composition of the layers was selected from the Fe/Co-Si-B and Fe-Cu-Nb-Si-B systems, respectively. Ribbons with typical thickness of 45-50 microns and width of 6 mm and 10 mm exhibited amorphous structure of both layers in as-quenched state. Temperature dependencies of electrical resistivity, dilatation and magnetization have been investigated in the amorphous state and during crystallization of both layers, which take place at different temperatures. The results combined with investigation of the structures formed in each layer and at the layer interface were compared to those of single-layer ribbons having the compositions of each layer, respectively.

Abstract: Structure as well as magnetic and magnetoelastic properties of nanocrystalline (Fe,Co)-(Hf,Zr)-Cu-B alloys (HITPERM-type) were investigated in order to find out which factors are responsible for the magnetic hardening of these magnetically soft materials. Magnetoelastic anisotropy, caused by the presence of cobalt, was found to play the predominant role in the observed increase of coercive field. On this basis, guidelines on chemical composition and crystallisation process selection were suggested for two fields of application: soft magnetic cores and sensors or actuators cores.