Papers by Author: Giora Kimmel

Abstract: The Heusler alloys Ni50Mn25+xGa25-x display magnetic shape memory effect (MSM) with very fast and large reversible strain under magnetic fields. This large strain and the speed of reaction make MSM alloys attractive as smart materials. Our crystallographic investigation of these alloys, focused on non-stoichiometric composition with excess of manganese. Using neutron diffraction, we revealed the necessary processing parameters to achieve and preserve the homogeneous metastable one-phase martensitic structure that is needed for an MSM effect at room temperature.

Abstract: The following nanocrystalline binary oxide systems were studied: Mg-Ti, Ni-Ti, Zr-Al, as well as some pure and doped unary oxides. The xerogels were heated at a constant T (200 to 1600°C) for 3 to 6 hours. There was a threshold tempearture for oxide formation and in many cases the products were metastable nanocrystalline phases, depending on the grain size and composition, including doping. The oxide phases of Ni-Ti, Mg-Ti, and Zr-Al, formed at 900 °C are different from those formed at higher temperature. New ranges of solid solutions and the formations of higher temperature structures were found. A transition phase can be defined as a structure formed at relative low tempearture, irreversibly transforming at higher temperature into an equilibrium phase of the same elemental composition. Some low temperature transition phases have a structure similar to that of a high temperature equilibrium phase, e.g., (the equilibrium phase is given in parentheses) tetragonal ZrO2 (monoclinic) and low-T qandilite-like solid solutions (qandilite + geikielite). Others are unique with no representation in the equilibrium phase diagram, e.g., gamma-like alumina (corundum) and anatase (rutile), which are formed as nanocrystalline oxides due to a low growth rate caused either by a low temperature of calcination or due to additives. To asses the importance of crystal size in the stabilization of transition phases, the following studies were undertaken: (a) XRPD analysis of all unary, doped and binary compositions; (b) the evolution of transition phases in HT XRPD of the Mg titanates; (c) the phase evolution was studied with time at temperatures were mixtures of transition and equilibrium phases were found; (d) the retention of pure tetragonal ZrO2 on quenching Al-Zr oxides after calcinations at high tempetature; (e) additional evidence from HRTEM, SEM and DTA experiments was also collected. A model, correlating the size effect with the unusual phases and structures is proposed.