Papers by Author: Guan Ling Su

Abstract: By introducing self-pressure processing into combustion synthesis under high gravity, Al2O3-ZrO2(4Y) eutectic composite ceramics without shrinkage cavities and holes were achieved, and the self-pressure processing also made the macro-crack be controlled and the ceramic densification be promoted evidently. XRD results showed the eutectic ceramics were composed of α-Al2O3, t-ZrO2 and a few m-ZrO2 phases, and the volume fraction of the transformable t-ZrO2 increased with self-pressure force increasing. SEM images showed that with increasing self-pressure force, the rod-shaped eutectic colonies were refined and the volume fraction of the colonies increased. Meanwhile, the irregular ZrO2 crystals around eutectic colonies transformed to be fine t-ZrO2 spherical crystals gradually, and thickness of eutectic colonies decreased. With the changes in microstructures of the ceramics, the mechanical properties of the ceramics were improved greatly.

Abstract: Large bulk solidified TiC-TiB2 eutectic composite ceramics were prepared by combustion synthesis under high gravity, and the WO3 was introduced into the combustion synthesis as one of oxidants in thermit to obtain the Ti-W-Cr-C-B liquid, so near-full-density TiB2-(Ti,W)C eutectic composite ceramics without the macrocracks were achieved. The ceramic matrix was mainly composed of TiB2-(Ti,W)C eutectic microstructures, and a few of Al2O3 and Al2O3-ZrO2 eutectic structures were also detected in between Ti-W carbides. Due to the introduction of the high gravity field, Stocks immigration of the immiscible liquids took place due to their density differences, resulting in float-up of oxide liquid and settle-down of Ti-W-Cr-C-B liquid, and the layered melt consisting of oxide liquid and Ti-W-Cr-C-B liquid was formed, finally, TiB2-(Ti,W)C eutectic composite grown from the melt. Due to the mutual solubility of W-Ti, the W atom diffused into the TiC, leading to the formation of (Ti,W)C solid solution as same as crystal lattice structure of TiC. The relative density, Vickers hardness and fracture toughness of the composite ceramics measured 98.4%, 26.4 GPa and 7.6±0.5 MPa•m1/2, respectively.

Abstract: (Ti, W)C matrix metal ceramics were prepared through combustion synthesis under high gravity, structure formation mechanism of the ceramics was discussed and the properties of the ceramics were also measured. XRD and FESEM images show the matrix of metal ceramics was mainly composed of TiC and (Ti, W)C1-x. The formation mechanism mainly involves two stages: firstly, combustion reaction is advanced rapidly under high gravity, and the layered melt consisting of Ti-W-Fe-C-B liquid at the bottom and oxide liquid at the top is formed due to rapid liquid-liquid separation under high gravity, subsequently, TiC solids as the primary phase precipitates from Ti-W-Fe-C-B liquid due to the higher concentration and faster diffusion of C relative to B in the alloy liquid, whereas (Ti, W)C1-x solid nucleates and grows on the surface of TiC solids. The Vickers hardness, flexural strength and fracture toughness of the (Ti, W)C matrix Metal ceramics measured 25.6 GPa, 1060 MPa and 8.5 MPa•m1/2, respectively.

Abstract: The large bulk Al2O3/ZrO2 (Y2O3) eutectics were achieved by combustion synthesis in high-gravity field. With increasing high-gravity level, the matrix of eutectics transformed the rod-shaped colonies from the cellular ones, and the nanocrystalline microstructures came into existence as the high-gravity level was larger than 200g. The relative density, hardness, flexural strength and fracture toughness increased simultaneously with increasing high-gravity level, and reached the maximum values of 98.6%, 18.6GPa, 1248MPa and 15.6MPa•m1/2 respectively as the high-gravity level was 250g.