Abstract: In the study, thermal efficiency in MIG welding of aluminum alloy with longitudinal magnetic field was analyzed, as well as softening behavior of heat-affected zone (HAZ) and base metal were investigated. The results showed that welding current decreased and resultingly total heat input reduced as the exciting current increased, meanwhile arc thermal efficiency increased and melting efficiency decreased. As a result of action of the magnetic field, the trend of grain growth of HAZ slowed down and the influence on base metal of heat input decreased. When the exciting current was 20A, microhardness of HAZ and base metal improved evidently. However, as the exciting current continued to increase, the effect of magnetic field on softening behavior did not change significantly.

Abstract: Adhesive is an important part of ceramic-metal composite armor. In order to obtain excellent ballistic performance, some adhesive with a variety of content of nano-SiO2 was prepared, and mechanical properties and ballistic test were conducted. The results show that the pores in adhesive decrease the strength of the adhesive, and the fracture happens along with the pores. To add nano-SiO2 in adhesive can decrease the porosity and the scale of the pores. In the ballistic performance, the adhesive enhance the acoustic impedance, the greater acoustic impedance can increase the energy of transmission wave and decrease the energy of reflection wave, leading to that the ceramic is destroyed slightly. The targets with adhesive added in 20% nano-SiO2 express the best anti-bullet properties. There are so many big blocks left in targets and the height of back convex is only 2.36mm.