Abstract: Degradation and disintegration of the nickel base cermet anode is a serious problem in direct utilization of hydrocarbon fuels, especially for liquid fuels such as kerosene. Cell operation test was carried out for the SOFC with nickel – scandia stabilized zirconia (Ni-ScSZ) cermet anode by direct feeding of several liquid hydrocarbons at 1073 K at S/C = 2.0. For n-dodecane (C12H26) fuel, hydrogen produced by reforming reaction on the anode was mainly used for electrochemical oxidation reaction. In contrast, for desulfurized kerosene test, cell operation was only possible by lower current density. Furthermore, noticeable nickel particles growth occurred. This nickel sintering should be enhanced by remaining minor impurities, including sulfur, in the desulfurized kerosene. From the thermodynamic consideration, Ni-S eutectics can be stably formed under some SOFC operation conditions with 100 ppm of sulfur. Carbon deposition was observed on the nickel surface for both Ni-yttria stabilized zirconia (YSZ) and Ni-ScSZ systems, but was noticeably suppressed for Ni-gadolinia doped ceria (GDC) system.

Abstract: The electrochemical reaction of solid oxide fuel cells (SOFCs) was reviewed in terms of mass and charge transports of reaction species around the electrode/electrolyte interfaces. Oxygen reduction and fuel oxidation were analyzed by isotope labeling and secondary ion mass spectrometry as well as conventional electrochemical method. The SIMS images after 18O2 (stable isotope oxygen) labeling suggested that the O2/cathode/electrolyte interfaces were the most active parts for oxygen reduction and incorporation. The widths of active parts of oxygen reduction were about several 100 to some 1000 nm different depending on the cathode materials and reaction mechanism. The isotope labeling-SIMS technique was also applied to visualize the active parts for CH4 decomposition and carbon deposition around the anode metal/electrolyte oxide interfaces. The active parts for carbon deposition were only on the Ni surface on YSZ electrolyte. The effect of substrate oxide on the carbon deposition was also examined at the mesh-shaped metal/oxide interfaces.

Abstract: Oxygen diffusion was measured at oxygen/cathode/electrolyte interfaces and at oxide scales/alloy interconnects in Solid Oxide Fuel Cells (SOFCs). A stable isotope oxygen exchange technique (16O/18O exchange) was adopted to label the diffusion profiles in the oxides, and secondary ion mass spectrometry (SIMS) depth profiles were examined to determine the diffusion coefficients in the oxide ceramic materials. Diffusivity of oxygen in LaMnO3 cathode was measured under polarized condition (that is, considering the electrochemical process and diffusion). Also, oxygen diffusion in the oxide scales formed on the alloy was measured to clarify the formation mechanism of oxide scale.