Abstract: Aluminium and its alloys are used in all bare overhead energy transmission lines. Researchers and manufacturers, have in the past, made significant improvements in the tensile strength and conductivity of overhead lines. In the present work, the effect of heat treatments on the tensile strength of Al-Zr alloys (Al-0.15, 0.20, 0.25wt.%Zr) has been investigated (all compositions hereafter are described in wt.%). The Al-Zr samples were prepared by using a melt furnace and a continuous casting line. The cast, extruded and drawn samples with different diameters (4, 6, 10 mm) were aged isothermally and isochronally in muffle and tube furnaces. Aging was performed over a wide range of temperatures (350-450 °C) at constant aging times (100 hrs., 125 hrs.) and over a wide range of aging times (50-150 hrs.) at a constant temperature (425 °C). It was found that, aging temperatures, aging times, composition, processing techniques and size of the samples affect the tensile strength.

Abstract: Different kinds of Al and Al alloys are used for all bare overhead energy transmission lines. In the present work, the effect of heat treatments on the conductivity of Al-0.25wt.%Zr alloy has been investigated. Al-0.25wt.%Zr samples were prepared in cold graphite crucibles by using a vacuum furnace and a continuous casting line. The samples were aged isothermally and isochronally in muffle and tube furnaces. Aging was carried out at a wide range of temperatures (350-600 °C) at constant aging times (75 h, 100 h) and a wide range of aging times (25-500 h) at constant temperatures (425 °C, 450 °C). According to the experimental results, conductivities of aged samples increase up to a certain aging temperature and aging time and reach peak values, then decrease with increasing aging temperature and aging time.