Abstract: The feasibility of fabricating h-BN-SiC high-temperature ceramics by in-situ combustion synthesis was demonstrated by igniting the mixture of boron carbide and silicon powder under 100MPa nitrogen pressure. The reaction thermodynamics and the adiabatic combustion temperature were calculated theoretically. The phase composition, microstructure and mechanical properties of composite were identified by XRD and SEM. The maximum bending strength and fracture toughness of the composite were 65.2 MPa and 1.4 MPa·m1/2 under room temperature, respectively. The effects of h-BN and SiC dilution contents on the mechanical properties of composite were also discussed.

Abstract: The fabrication of AlN-SiC-TiB2 ceramics with powder mixtures of Al, 6H-SiC and TiB2 was investigated by self-propagating high temperature synthesis (SHS) and hot isostatic pressing (HIP). The powder mixtures were shaped by isostatic cool pressing method and the combustion reaction was carried at the pressure of 100-200 MPa N2 by an ignitor. The compositions and morphologies of the combustion product were studied by XRD and SEM. The determined bending strength and the fracture toughness of the ceramics were 350 MPa and 3.5 MPa⋅m1/2 respectively.