Papers by Author: Hong Xiu Du

Abstract: The mechanics properties of HPC mixing different dosage and length of polypropylene fiber were investigated in this study. The results showed that the addition of appropriate amount and length of polypropylene fibers in HPC led to an effective improvement in the tensile strength and a little change in the compressive strength of HPC. The pronounced improvement can be attributed to the beneficial effect of polypropylene fiber on HPC by restraining the generation and development of the micro cracks in concrete, enhancing the level of stress and deformation and damage characteristics in HPC, furthermore, extending the durability and safety of concrete structure.

Abstract: An experimental research was performed on the compressive strength and splitting tensile strength for HSC with various polypropylene（PP） fibers after exposure to temperatures 300°C, 500°C, 700°C, 900°C. Cubes of 150mm×150mm were designed and fabricated with C60, blended with silica fume and slag, mixed with PP fibers, respectively. These specimens were naturally cooled to room temperature after being heated in an electric furnace. No explosive spalling was observed during the fire test on all HSC with PP fibers. From the results of nine types of concretes, both the compressive strength and splitting tensile strength of HSC with PP fibers decreased with the increase of temperature. Through a series of measurement, the relationships between the mechanical properties and the various PP fibers in HSC were analyzed, including the dosage and length of PP fiber. Based on the comparison in the experimental results, the proposed optimum of PP fiber in HSC was 1.5kg/m3 under the test condition. In addition, PP fiber with the length of 8mm could be more applicable to use.