Abstract: In this paper, microstructure of AL-Cu eutectic alloy is simulated by improving Nestler’s multiphase-field model. The exact physical parameters are used in multiphase-field model, and obtained the steady calculational results. In this numerical calculation, AL and AL2Cu are regard as two independent components. The eutectic microstructure is regard as an admixture of single phase α (AL) and single phase θ (AL2Cu). Using the model, steady eutectic layered growth is simulated, and the simulated results agree well with the solidification theory. At the same time, the stochastic noise is introduced, and eutectic free layered growth microstructure is simulated. The microstructure of primary dendritic crystal and pseudoeutectic is also simulated by enlarging the calculational interval scale, and obtained a better result.

Abstract: The effect of the combined action of hot work and heat treatment on the microstructure and mechanical properties of a Mg-2Gd-Nd-0.4Zn-0.3Zr (wt. %) (E21) alloy was investigated. Results showed that the solution treatment time of the ingot played a great effect on the mechanical properties of the extruded alloy. With solution treating time of the ingot increasing, the tensile strength of the extruded alloy decreased gradually, but the elongation increased greatly. The best combination of strength and ductility was achieved for the extruded alloy after the ingot solution treated at 520°C for 3 h, extrusion at 400°C and aging at 200°C for 16 h, namely ultimate tensile strength = 331MPa and elongation = 7.1%.