Papers by Author: Hui Cong Liu

Abstract: Titanium alloys has been widely used in many fields, while in high temperature and rigorous corrosive environment, it is very necessary to do some work on the surface of titanium alloys to satisfy with application purpose. In this paper, four kinds of sol film were prepared on titanium alloys with and without anodic oxidation film. The prepared sol included Al2O3, Al2O3-ZrO2 and doped sol by adding additive into them respectively. The film thickness, high temperature oxidation resistance and corrosion resistance after high temperature oxidation for some time were investigated. The results show that the sol film obtained on the anodic oxidation film of titanium alloys is thicker than that without anodic oxidation film. Compared with the other three kinds of film, the doped Al2O3-ZrO2 sol film has the best high temperature oxidation resistance and corrosion resistance due to insulation effect of the sol film, and the composition of additive and zirconic.

Abstract: In this paper, the anodic oxidation film was prepared in the 1~3mol/L NaAlO2 solution with and without silicon sol added. The film thickness, high temperature oxidation resistance, corrosion resistance, and SEM image, element composition in the film were investigated. The results show that there were obvious improvement in high temperature oxidation resistance and corrosion resistance of the film on titanium alloys after adding silicon sol into the NaAlO2 solution, and with the sol percentage in the solution increased, the foregoing protection abilities of the anodic oxidation film became better, while the film thickness was little affected with the sol percentage difference. The reason was discussed and the effective factor was the silicon composition and more even and compact image in the film.