Abstract: Nickel powders were synthesized by the reduction of hydrazine of nickel salts from diethanolamine (DEA) solution, and the morphological characteristics of nickel powders were investigated with various process conditions such as the addition of hydrazine, reaction temperature, the composition of mixed solvents. The addition of hydrazine in DEA solution largely affected the size control of nickel powders. Under N2H4/Ni2+molar ratio= 1.5 and 2.0 conditions, spherical nickel powders in the submicron range were obtained owing to higher the reduction rate. An increase of temperature increased the size of nickel particles. At 220°C for 40min, the nickel powders were composed of polyhedral particles with a high crystalline in the submicron range. The mixed volume ratio of TEA to DEA solvent improved the inhibition of agglomerate between particles.

Abstract: Nickel powders were prepared by the reduction of hydrazine of Ni(OH)2 reactant slurries from non-aqueous media. The morphological characteristics of nickel powders were investigated under various processing conditions. Nickel powders were characterized by using scanning electron microscope (SEM), X-ray diffractometer (XRD), thermal gravitational analysis (TGA) and X-ray photoelectron spectroscopy (XPS). The size of nickel powders was increased as the reaction temperature and time increased because of the thermal agglomeration of nuclei and/or increased growth rate. The surface of nickel powders composed of both Ni and Ni(OH)2 was oxidized in the temperature range of 400-600°C.