Abstract: The biological behavior of a new bioactive material composed of calcium-deficient hydroxyapatite, octacalcium phosphate, and β-tricalcium phosphate was investigated by in vitro indirect and direct cytotoxicity, cell adhesion and proliferation tests, and by in vivo subcutaneous and bone implantation in rats. The results of the in vitro studies showed that the material is biocompatible and no cytotoxic. Slightly poorer initial cell adhesion and lower cell proliferation than in control was observed, which were attributed to the reactivity and roughness of the material surface. In vivo results showed that the material is biodegradable and bioactive in bone tissue, but only biocompatible and partially biodegradable in soft tissue.

Abstract: In this work a new kind of CaSiO3-doped α-Ca3(PO4)2 ceramic materials, with compositions lying outside the field of the Ca3(PO4)2 solid solution in the system Ca3(PO4)2- CaSiO3, were obtained and some of their properties, relevant for bone repairing, were studied in vitro. Crystalline α-Ca3(PO4)2 solid solution and minor amounts of non-equilibrium residual glass were the only phases in the materials containing 2 and 5 wt% of CaSiO3. α-Ca3(PO4)2, crystalline eutectic-like phase and residual glass were observed for sample containing 15 and 20 wt% of CaSiO3. The mechanical strength improved for all the doped ceramics with regard to un-doped Ca3(PO4)2. The release of ionic Ca and Si in simulated physiological conditions increased with the content of CaSiO3 and favored α-Ca3(PO4)2 surface transformation. The soluble components extracted from the CaSiO3-doped α-Ca3(PO4)2 bioceramics were not cytotoxic to human fibroblastlike cells. Initial cell adhesion onto the surface of the materials seemed to be partially hindered by surface reactivity and remodeling, however those cells adhered to the experimental bioceramics were viable and proliferated normally.