Papers by Author: Jean Lorenzzi

Abstract: In this work we report on SiC epitaxial growth by vapour-liquid-solid (VLS) mechanism on on-axis 4H-SiC(0001) substrates which were previously patterned to form mesa structures. The liquid phase was set to Al70Si30. At 1100°C, it led to very high homoepitaxial lateral growth (140 µm/h) with pronounced spiral growth and in plane anisotropy of growth rate. Upon temperature increase to 1200 °C, this spiral growth was suppressed and the lateral growth was further increased up to 180 µm/h. The in-plane versus out-of-plane anisotropy of growth rate was found to be as high as 60 at this temperature and 46 at 1100°C.

Abstract: In this work we report on the study of twin boundary (TB) evolution during heteroepitaxial growth of 3C-SiC on patterned 4H-SiC(0001) substrate by vapour-liquid-solid (VLS) mechanism. Ge₅₀Si₅₀ melt was used at a temperature of 1450°C. 3C-SiC deposit was obtained on top and outside the mesas. Some lateral enlargement of these mesas was observed but it was systematically homoepitaxial. Elimination of TBs inside the 3C-SiC deposit on top of the mesas was observed for specific mesa shape and/or orientation of the sidewalls. Though three–fold or six-fold symmetry mesas are recommended for TB elimination, originally circular mesas lead also to the same result due to initial faceting toward hexagonal shape.