Papers by Author: Ji Bing Li

Abstract: Transition metal-modified carbon-based adsorbents were prepared by impregnating activated carbon with solutions of copper, cobalt or nickel chloride or nitrate. The mixtures were dried and then calcined under nitrogen stream. The surface metal species were analyzed by XRD technique and the surface oxygen-containing groups were characterized by FTIR. Their adsorption capacities for dibenzothiophene (DBT) were measured by using DBT-containing n-octane solution as model oil. Experimental results show that the metal species on the carbon surface could be controlled by the calcination process under nitrogen atmosphere. Both the transition metal precursors and kinds of metal species on the carbon surface have significant effects on DBT adsorption capacity.

Abstract: Phosphotungstic acid (HPW) supported on activated carbon (AC) combined with hydrogen peroxide formed an oxidative desulfurizaiton (ODS) system to oxidize sulfur-containing compounds in diesel fuel. Dibenzothiophene (DBT) dissolved in n-octane was selected as a model feedstock for studying this new ODS system. The HPW/AC catalysts were characterized with XRD, FTIR and N2 adsorption-desorption measurements. HPW was highly dispersed on the surface of carbon support. It was found that the DBT adsorption capacity decreased from 42 mg S/g to 33.13 mg S/g as HPW loading amount increased from 0 to 15 wt.%. Oxidative removal of DBT in the model oil significantly increased with increasing HPW loadings on the support from 0 to 10 wt.%. 100 % DBT was removed by using the catalysts with HPW content higher than 10 wt. %. At 80 °C, oxidative removal of DBT reached 100 % after 40 min of reaction when O/S molar ratio ranged from 4 to 10.