Papers by Author: Jian Wei Chang

Abstract: The corrosion behavior of GW63 (Mg-6wt.%Gd-3wt.%Y-0.4wt.%Zr) alloys in 5% NaCl aqueous solution has been investigated by PARSTAT 2273 instrument. The Open Circuit Potential (ECORR) vs. time curve, cyclic polarization (Pitting Scans) curve and Electrochemical Impedance Spectroscopy (EIS) was measured for the GW63 alloys in as-cast and T6 heat treatment conditions. The EIS results indicated that the tendency of impedance variation for as-cast condition was monotonic decreasing, however, the tendency of variation for T6 condition was not completely monotonic but the total tendency was decreasing. The values of impedance of GW63 alloy at 0.1 Hz are about 103 ohm-cm2 for as-cast and T6 condition.

Abstract: The microstructure, mechanical properties, creep and corrosion resistance of Mg-Gd-Y-Zr(-Ca) alloys were studied. Small additions of 0.4-0.6 wt% Ca to Mg-(9-10)Gd-3Y-0.4Zr(wt.%) alloys led to a slight improvement in creep resistance and a remarkable increase in corrosion resistance, but an obvious decrease in elongation to fracture. UTS and TYS of the Mg-Gd-Y-Zr(-Ca) alloys are obviously higher than those of WE54, especially in the temperature range from room temperature to 200 oC. TEM images and corresponding energy dispersive x-ray spectra showed that the Ca element primarily segregated to the grain boundaries and existed in the cuboid-shaped particles with a trace concentration, and the small addition of Ca had no obvious effect on the orientation, morphology, and distribution of β′ phase, which is responsible for the peak hardness in Mg-Gd-Y-Zr alloys.