Papers by Author: Jin Gee Park

Abstract: Titanium and its alloys are difficult-to-form materials due to limited slip system and plastic anisotropy. Titanium is also prone to change in color due to oxidation at high temperatures. It is thus advisable to conduct deep drawing of titanium and its alloys at temperatures below 600°C. In this study, the drawability of Ti-6Al-4V sheet is evaluated in respect to the process parameters such as forming temperature, forming speed, and blank holding force at elevated temperatures. It is shown that the limit drawing ratio (LDR) increases with increasing temperature, but varies insignificantly with forming speed. The development of residual stresses in the wall of drawn cups during deformation was evaluated.

Abstract: Titanium alloy sheets have excellent specific strength and corrosion resistance as well as good performance at high temperature. Recently, titanium alloys are widely employed not only aerospace parts but also prosthetics and motorcycle. However, titanium and its alloys are difficult-to-form materials due to limited slip system and plastic anisotropy. Titanium alloy sheets were usually formed by slow forming or hot forming with heating die and specimen. In the sheet metal forming area, FE simulation technique to optimize forming process is widely used. To achieve high accuracy FE simulation results, identification of material properties and deformation characteristics such ad yield behaviors are very important. In this study, the yield locus of Ti-6Al-4V sheet was obtained at warm temperature. The experimental results are compared with the theoretical predictions. Also, the Forming Limit Curves (FLC) was achieved at warm temperature.