Papers by Author: Jun Ying Lai

Abstract: In this paper the influence of mineral admixtures on early shrinkage of ordinary concrete with the same water-binder ratio is studied by self-made equipment and CABR-NES deformation instrument developed by China Academy of Building Research Institute. All concrete specimens are cured with one surface exposed to air and others are covered with plastic film. The replacement ratio of mineral admixtures is 10%, 20% and 30%, respectively, and a mixture of a combination of both fly ash and slag is also studied. The results indicate fly ash reducing the early shrinkage of ordinary concrete, and the shrinkage decreases with the increasing of replacement ratio, but the effect is not so significant when the replacement ratio is above 20%. Slag also reduces the early shrinkage of ordinary concrete, and the shrinkage decreases with the increasing of replacement ratio, but the effect is not so significant when the replacement ratio is below 20%. Mixture with a combination of both fly ash and slag has lower shrinkage than mixture with fly ash.

Abstract: To improve the accuracy of parameter identification and to reduce the test cost in the high-rise structure health monitoring systems , the paper proposes an optimal placement method combines genetic algorithms with improved information matrix criterion (GA-IIM). With traditional improved effective independent method (EFI-DPR), it is easily trapped into bureau of optimum solution, and the proposed method can resolve this problem. The solutions were coded by a two-dimensional integer array, each line stored a feasible solution and compulsory mutation was adopted to avoid the solution reappeared in the same position. To improve the convergence speed, each generation of optimal group was kept to the next one to participate in the competition. With the improved information matrix criterion embedded in the genetic algorithms, the placement design was produced. This technique was used to optimize the sensor placement of a nineteenth layer frame structure. Comparing the optimized sensor placement of the proposed method with that of improved effective independent method by the modal assurance criterion and the mean square error, the proposed method performs better.

Abstract: In order to study the influence of modified polypropylene (PP) fiber on the physical and mechanical properties of curing sludge, the same amount of cement and different content of polypropylene fiber were mixed into the sludge. Unconfined compressive strength tests, water content tests and shear strength tests were carried out on different specimens with different curing time. The results show that the sludge curing effect is markedly improved by the addition of the polypropylene fiber. As to the curing sludge with the same curing time, when the content of the polypropylene fiber increases, the unconfined compressive strength and the cohesive strength greatly increase, and the internal frictional angle decreases.

Abstract: Concrete durability is one of the most important considerations in the design of new structures in aggressive environments. It generally depends on the quality of the concrete surface and the cracks of concrete. In this paper, the rebound numbers of concrete cast using controlled permeability formwork (CPF) and ordinary steel formwork were determined. And the early age shrinkages of concrete cured in dry environment of 20±2°C, 75±5% RH, in sealed condition with plastic film and in covered condition with CPF liner were measured. Testing results indicated that CPF could improve the concrete surface hardness and reduce the early age shrinkage of concrete. So CPF can enhance concrete durability and prolong its life-span.

Abstract: The environmental fire retardant mentioned in this paper was compounded of disodium octaborate tetrahydrate and silicon dioxygen(SiO2)gels. Specimens of Chinese fir were impregnated with the compound by pressure and its fire retardant performance was studied. Results showed that, the anti-loss performance of disodium octaborate tetrahydrate was improved obviously. Compared with the untreated specimen, total heat release of the treated specimens decreased by 44.5% on average, while heat release rate decreased by 50.85% on average and ignition time prolonged obviously, which indicates that this compound possess good fire retardancy effect

Abstract: A series of water-soluble polycarboxylate-type superplasticizer (PCA) were synthesized by free-radical copolymerization of methyl acrylic acid and methoxy poly(ethylene glyco1) monoacrylate macromonomers in water solutions．Micelles were formed from the resultant PCA with predetermined hydrophobic and hydrophilic blocks in water. The hydrodynamic diameter and size distribution of micelles were determined by dynamic light scattering. The change of the concentration of the electrolyte results directly in the variation of the dispersing force of PCA in cement paste. The dispersing force degrades with increasing electrolyte concentration.