Abstract: The effect of slurry composition and wafer flatness on a material removal rate (MRR) and resulting surface roughness which are evaluation parameters to determine the CMP characteristics of the on-axis 6H-SiC substrate were systematically investigated. 10 x 10 mm2 6H-SiC substrates and 2-inch SiC wafers fabricated from the ingot grown by a conventional physical vapor transport (PVT) method are used for this study. The SiC substrate after the CMP process using slurry added oxidizers into slurry consisted of KOH-based colloidal silica and nano-size diamond particle exhibited the significant MRR value and a fine surface without any surface damages. SiC wafers having high bow value after the CMP process exhibited large variation in surface roughness value compared to wafer with low bow value. The CMP-processed SiC wafer having a low bow value of 10m was observed to result in the MRR value of 0.15 m/h and the mean height (Ra) value of 0.772Ǻ.

Abstract: 2inch 6H-SiC (0001) wafers were sliced from the ingot grown by a conventional physical vapor transport (PVT) method using an abrasive multi-wire saw. While sliced SiC wafers lapped by a slurry with 1~9㎛ diamond particles had a mean height (Ra) value of 40nm, wafers after the final mechanical polishing using the slurry of 0.1㎛ diamond particles exhibited Ra of 4Å. In this study, we focused on investigation into the effect of the slurry type of chemical mechanical polishing (CMP) on the material removal rate of SiC materials and the change in surface roughness by adding abrasives and oxidizer to conventional KOH-based colloidal silica slurry. The nano-sized diamond slurry (average grain size of 25nm) added in KOH-based colloidal silica slurry resulted in a material removal rate (MRR) of 0.07mg/hr and the Ra of 1.811Å. The addition of oxidizer (NaOCl) in the nano-size diamond and KOH based colloidal silica slurry was proven to improve the CMP characteristics for SiC wafer, having a MRR of 0.3mg/hr and Ra of 1.087Å.