Papers by Author: K.S. Kim

Abstract: The fatigue life data obtained under stress control conditions with and without mean stress are interpreted with reference to mean stress and ratcheting effects. Tests are conducted on nickel-base super-alloy Inconel 718 at 649°C and copper alloy Elbrodur-NIB at room temperature. The ratcheting strains at failure are obtained, and mean stress models such as the modified Goodman equation, the Smith-Watson-Topper parameter, and the Walker parameter are evaluated. The results are discussed in comparison for the two materials.

Abstract: Crack growth in compact specimens of type 304 stainless steel is studied at 538oC. Loading conditions include pure fatigue loading, static loading and fatigue loading with hold time. Crack growth rates are correlated with the stress intensity factor. A finite element analysis is performed to understand the crack tip field under creep-fatigue loading. It is found that fatigue loading interrupts stress relaxation around the crack tip and cause stress reinstatement, thereby accelerating crack growth compared with pure static loading. An effort is made to model crack growth rates under combined influence of creep and fatigue loading. The correlation with the stress intensity factor is found better when da/dt is used instead of da/dN. Both the linear summation rule and the dominant damage rule overestimate crack growth rates under creep-fatigue loading. A model is proposed to better correlate crack growth rates under creep-fatigue loading: 1 c f da da da dt dt dt Ψ −Ψ     =         , where Ψ is an exponent determined from damage under pure fatigue loading and pure creep loading. This model correlates crack growth rates for relatively small loads and low stress intensity factors. However, correlation becomes poor as the crack growth rate becomes large under a high level of load.

Abstract: The crack growth behavior in a 304 stainless steel has been investigated at 538°C in air environment. Compact tension specimens were subjected to fatigue, creep and creep-fatigue loading. The combined effects on crack growth rates of load level and hold time have been examined. Stress intensity factors are found to correlate crack growth rates reasonably well for fatigue crack growth. Creep crack growth rates are found to correlate with stress intensity factor and C*(t). Crack growth rates under hold time cycles are successfully correlated with C*(t)avg under various load levels and hold times. Crack growth under creep-fatigue loading has been simulated by elastic-plastic-steady state creep finite element analyses. The results of analysis show that fatigue loading interrupts stress relaxation around the crack tip during hold time and causes stress reinstatement, thereby giving rise to accelerated crack growth compared with crack growth under static loading. Analysis of hold time crack growth based on the cyclic stress-strain response yields crack closure during unloading, and creep deformation during hold time tends to lower the closure load.