Papers by Author: Ludmila Kučerová

Abstract: In- situ testing is a new and progressive method of material analysis, which can offer new information about behavior of individual phases and structural components in metals. Local mechanical properties or strain distribution can be directly obtained for fine multiphase microstructures. The second application of in-situ stages lies in observation of phase transformations that occur either during heating, cooling or straining of metals. EBSD analysis can be also performed during in-situ testing if the stage allows tilting of the sample toward EBSD detector. Preparation of samples for in-situ testing is of the utmost importance for successful analysis. This work concentrated on sample preparation techniques used for flat samples of 42SiCr steel. Preliminary in-situ cold deformation tests of this steel with EBSD acquisition and observation of microstructure development were also carried out.

Abstract: Three low alloyed transformation induced plasticity (TRIP) steels with 0.2%C were used in this work. The first one was based on the most common and popular 0.2%C - 1.5%Mn - 1.8%Si concept and was used as a reference material. The second steel was further micro-alloyed by 0.06% of Niobium. The third steel was designed with lower manganese content of 0.6% and additional alloying by 0.8% of Chromium. Thermo-mechanical processing with incorporated incremental deformation was applied to each steel. Various cooling rates and numbers of deformation steps were tested with regard to final microstructure and properties. After this optimization, microstructures with the potential to utilize TRIP effect were achieved for all steels. Very good mechanical properties were obtained with ductility typically in the interval of 30-40% and the tensile strengths in the range of 680-835 MPa.

Abstract: The cold formability of ferritic-pearlitic steels is one of the base parameters for material choice for different forming parts. One of the key factors is the pearlite morphology, which is strongly dependent on chemical composition and previous treatment history. The carbides in pearlite occur mainly in the lamellar form. One of the ways of improving the ductility along with formability is the change of lamellar carbides to globular carbides. This can be conventionally done by soft annealing, which is characterised by long processing times and high energy costs. This paper presents a new processing modification which can lead on the one hand to significant shortening of carbide spheroidization times and on the other hand to intensive refinement of grain size even for low-carbon steels. Low temperature thermomechanical treatment with variation of the heating temperature around A_c1 and incremental deformation was examined on low carbon plain RSt-32 steel. After the thermomechanical treatment conditions were optimized, the refinement of the ferritic grains from an initial 30 μm to circa 5 μm took place, and the time necessary for carbide spheroidization was shortened from several hours to several seconds.

Abstract: The use of the combined influence of retained austenite and bainitic ferrite to improve strength and ductility has been known for many years from the treatment of multiphase steels. Recently, the very fine films of retained austenite along the martensitic laths have also become the centre of attention. This treatment is called the Q-P process (quenching and partitioning). In this experimental program the quenching temperature and the isothermal holding temperature for diffusion carbon distribution for three advanced high strength steels with carbon content of 0.43 % was examined. The alloying strategies have a different content of manganese and silicon, which leads to various martensite start and finish temperatures. The model treatment was carried out using a thermomechanical simulator. Tested regimes resulted in a tensile strength of over 2000MPa with a ductility of above 14 %. The increase of the partitioning temperature influenced the intensity of martensite tempering and caused the decrease of tensile strength by 400MPa down to 1600MPa and at the same time more than 10 % growth of ductility occurred, increasing it to more than 20%.

Abstract: The concepts new types of materials are, for economic reasons, focused mainly on low alloyed steels with a good combination of strength and ductility. Suitable heat and thermo-mechanical treatments play an important role for the utilization of these materials. Different alloying strategies are used to influence phase transformations. The quenching and partitioning process (Q-P Process) is one of the heat treatment methods which can result in a high ultimate strength as well as a good ductility. However, these good properties can be obtained only if a sufficient amount of retained austenite is stabilized. The influence of different contents of manganese, silicon and chromium on microstructural development and mechanical properties were experimentally tested. Alloying elements were used to stabilize the retained austenite in the final microstructure and also to strengthen the solid solution. Ultimate strengths of over 2000MPa with ductility over 10% were reached after the optimization of the Q-P Process. The microstructures were analyzed using several microscopic methods; mechanical properties were determined by a tensile test and the volume fraction of the retained austenite was established by X-ray diffraction phase analysis.