Abstract: In order to examine the correlation between a mechanical property and an excess free volume for metallic glass Pd44Cu31Ni8P17, longitudinal and transverse ultrasonic velocities were measured to estimate longitudinal and transverse elastic constants, c11 and c44. An as-quenched sample, an annealed one at a temperature just below a glass transition temperature Tg and a crystalline one were prepared. The as-quenched sample contains the excess free volume depending on the preparing process. The Young’s modulus E, the Poisson’s ratio, a bulk modulus and c12 are estimated using c11 and c44. The values of c11, c 44 , c12 and E of the as-quenched one are smaller than those of the annealed sample losing excess free volume by about 0.2 % and much smaller than those of the crystalline one. The Poisson’s ratio for the as-quenched sample and the annealed one are 0.389 and 0.387, respectively, which are much larger than that for the crystalline one with 0.349.

Abstract: In order to examine mechanical properties of a metallic glass Zr50Cu40Al10 in low temperature below room temperature, the temperature T dependence of mechanical resonance of ultrasonic wave are measured. The mechanical resonance frequency in an as-quenched sample shows an abrupt increase at 200K for longitudinal wave and 160 K for transverse wave with decreasing T. After this abrupt increase, the sound propagation cannot be detected below these temperatures but the wave propagation is restored with increasing T and there is an abrupt decrease at 260K for the both wave modes. The similar hysteresis is observed in temperature dependence of the electrical resistivity. These suggest a kind of structure instability of Zr50Cu40Al10 in low temperature region.