Papers by Author: M.K. Sarangi

Abstract: Deformation of Titanium alloys close to optimal superplastic condition i.e. near superplastic regime of deformation leads to significant change in microstructures.VT-9 titanium alloy was used in order to find out those parameters of microstructure which are varying significantly during near superplastic regime of deformation. Tensile tests were carried out at 930°C up to fracture with a constant strain rate of 5*10^-4 s^-1 and a jump wise varying strain rate of 1*10^-4 s^-1 & 5*10^-4 s^-1 .The microstructural parameters of both air-cooled and water quenched portion i.e. size of alpha phase, percentages of alpha phase and parameter of non-uniaxiality of alpha phase were found to change significantly during near superplastic regime of deformation. It has been found that in the near superplastic regime of deformation percentage of α-phase decreased from 90% to 13%. As the β-transus temperature of this alloy is 970°C, this significant change in percentage of α-phase is attributed to deformation induced phase transformation. Optical microscopes, micro Vickers hardness test, XRD, FESEM have been used to characterize the microstructure of the material.

Abstract: When deformations are carried out with fine grained microstructure and within a narrow range of strain rates and temperature, metals and ceramics have been shown to exhibit superplastic behavior. Under these conditions the material demonstrates unusually high elongation with a relatively stable microstructure. But when the above mentioned parameters lie beyond a limit, near superplastic behavior is observed. The microstructure changes actively during the process of deformation and the response of the material becomes dependant on the history of loading. A model to describe the dependence on loading history by taking into account the change in microstructure is proposed. The model predicts the general trends observed and also provides possible explanation to some of the effects observed in the experimental data.