Papers by Author: Madangopal Krishnan

Abstract: Evolution Texture and microstructure has been investigated in a Fe-14Mn-6Si-9Cr-5Ni shape memory alloy during cold rolling and annealing. The starting solution-annealed material show a nearly random texture with microstructure composed of equi-axed austenite grains with some e martensite plates inside. Cold rolling induces a strong alloy type texture with Brass {011}<211> and Goss {011}<100> as major components. Annealing of the cold deformed material produces a nearly random texture. The microstructural investigation reveals that with increasing cold deformation the amount of stress induced e and a’ martensite volume fraction increases. The electron back scattered diffraction (EBSD) phase mapping shows that reversion of the e martensite starts only after commencement of recrystallization.

Abstract: The thermal cycling (quenching in liquid nitrogen and reverting back to room temperature: austenite martensite reversible transformation) response of Ni-Ti-Fe shape memory alloys has been investigated. It was clearly noted that residual deformation, estimated in terms of noticeable differences in austenite grain size, depend on the relative clustering of fine grains. During repeated thermal cycling, the residual deformation, in-grain misorientation developments and retained martensite content scaled together: bringing out a clear picture of microstructural irreversibility.

Abstract: The kinetics of dissolution of ordered phase with Pt2Mo structure has been studied in two nickel chromium alloys – one without molybdenum and another with molybdenum - using differential scanning calorimetry. The activation energy for dissolution, determined using three nonisothermal approaches was found to be ~ 418 kJ /mole for both the alloys. This value agreed very well with the activation energy for coarsening of g″ precipitates in Ni-Cr-Mo matrix and is close to activation energy for mobility of chromium and molybdenum in complex nickel alloy matrix.