Abstract: Compositionally graded Ba(1-x)SrxTiO3 thick films were fabricated by the airflow deposition technique. Films displayed hysteresis translation along the polarization axis when driven by an alternating electric field. The trend of the hysteresis shift as a function of temperature is similar to the difference of DC currents measured when a positive and negative DC electric field is applied. The study suggests that the origin of this phenomenon lies in an asymmetry of the film conductance due to the presence of asymmetric Schottky contacts at the BaTiO3/Ag and Ag/Ba0.xSr1-0.xTiO3 interfaces.

Abstract: In this work attempts to prepare strontium-doped lanthanum manganites La1-xSrxMnO3 using microwave-assisted hydrothermal synthesis were undertaken from a mixture of lanthanum nitrate, strontium nitrate, manganese(II) nitrate, potassium permanganate and potassium hydroxide as a mineralizer. For x = 0.3, and x = 0.5, the perovskite obtained is not defined since both La0.7Sr0.3MnO3 and La0.5Sr0.5MnO3 phases are consistent with XRD spectra. While with x = 1.0, for the first time, hexagonal strontium manganite was prepared as blade-shaped crystallites with a narrow particle length distribution (range 3.75-7.75 μm) at 210°C using a treatment time of only 1 hour. Conventional hydrothermal synthetic routes require at least 24 hrs treatment time.