Abstract: A 100GHz planar helix with straight-edge connections slow-wave structure incorporating coplanar waveguide feed has been designed and fabricated. The proposed fabrication process can produce high-aspect-ratio planar helical structures which is essential for sheet electron beam traveling-wave tube application. The photoresists used in this process can be easily stripped after electroplating of three-dimensional structures.

Abstract: Sr(Bi1-xSmx)8Ti7O27 ceramics were prepared by Sm2O3-substitution for Bi2O3 through solid-state reaction route. The dielectric properties of the sintered bodies such as er, Q and tf were investigated. The ceramics were characterized by SEM, XRD, DTA and TG, which behaved high dielectric constant of 128 ~154 at the frequency of 10 GHz.

Abstract: The initial interactions of plasma-sprayed HA coating surface with osteoblasts was investigated. Two kind of post-treatment methods were been used for HA coating: (1) Heated in air at 650oC for 30 min, (2) Heated in water vapor at 125oC, 0.15Mpa for 6 hours. The third passage rabbit osteoblasts were cultured on the HA coating plates for 24 h. The results showed: The lower dissolution rate and more surface hydroxyl groups (OH-1) group in the HA coating resulted in greater numbers of adhered osteoblasts and higher cell activity, The post-water vapor treated HA coating have better biological behavior in vitro.

Abstract: Bonelike apatite coating on metal implants is an effective method to enhance bioactive properties of the metal surface. In the present study, the effectiveness of cathode deposition (CD) coating methods was investigated. And biomimetic deposition (BD) was also investigated as the parallel. The revised simulated body fluid (R-SBF) was chosen as an electrolyte and simulated body fluid. Both deposition methods could produce bonelike apatite coating on rough surfaces of the titanium. The uniformity of the CD coatings were better than the BD coatings’. And CD method was less sensitive to the condition of the titanium plate surfaces and much faster in the coating deposition. The spectra of FTIR showed that the characteristic peaks of CO3 2- apeared on the surface of ceramics, combined with spectra of XRD and SEM, it was concluded that a sertain thickness of bonelike apatite coating could be formed on the acided treatment (AT) titanium plate surfaces by CD method.

Abstract: A nano-grade hydroxyapatite/collagen composite was prepared by an in situ synthesis technique from calcium nitrate, diammoniun hydrogen phosphate, and a cowhide collagen sol at low temperature. XRD and TEM analyses of the composite indicated that crystals formed in the collagen fibril matrix were nanohydroxyapatite with low crystallinity. Biocompatibility of the composite was evaluated by in vitro cytotoxicity test and in vivo genotoxicity and sensitization test. No mutagenic activity of the composite was observed in mouse micronucleus tests. No evidence of dermal sensitization of the composite was found in guinea pig maximization tests. The results from a filter diffusion test indicated that the composite did not induce a cytotoxic behavior. All these results suggest that the composite has excellent biocompatibility.