Papers by Author: N.H. Idris

Abstract: Measurement of the ionic conductivity for the CA-NH4CF3SO3-DMC system was carried out at frequencies of 50 Hz to1 MHz and also at temperatures of 298 K to 313 K. The plot of log σ versus 1000/T shows a linear behavior suggesting that the samples obey the Arrhenius relationship. The electrical relaxation of the system was analyzed using the complex electric modulus M* of the sample with the highest ionic conductivity at various temperatures. The analysis of electrical modulus and dissipation factor (tan δ) shows that charge transport occurs through a hopping mechanism.

Abstract: The plasticized PEO-KOH films have been investigated using the electrochemical impedance spectroscopy (EIS), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The conductivity of films increased by about 2 orders of magnitude from 10-5 to 10-3 S cm-1 at r.t. on addition of 0.5 wt.% of ethylene sulphite (ES). The degree of crystallinity was calculated from the XRD patterns. SEM micrographs show that the plasticized films were porous. The highest conductivity of plasticized films at r.t. was (1.3 ± 0.2) x 10-3 S cm-1 for the film with 0.5 wt.% of ES content. The number density of mobile ions was shown to increase indicating that ES has dissociated more salts into ions and thereby increasing the conductivity.