Papers by Author: O.I. Lomovsky

Abstract: TiB2-43vol.%Cu nanocomposite powders with titanium diboride particle size 50-100 nm were cold and detonation sprayed in order to fabricate coatings on a copper substrate. The powders were produced by self-propagating high-temperature synthesis (SHS) followed by mechanical milling. The temperatures during spraying were calculated and the change in the nanostructure of the powders during spraying was studied: in cold sprayed coatings the size of TiB2 particles was well retained, in detonation sprayed coatings the growth of the particles was observed, the mode of spraying greatly affecting the microstructure and the size of the particles. The hardness of cold sprayed coatings was higher compared to detonation sprayed coatings. This research shows the future potential for development of coatings with submicron and nanostructure by cold and detonation spraying of powders produced by mechanical milling.

Abstract: TiB2-Cu composites in a nanostructured state are candidates for high-strength conductive and erosion-resistant materials. In this work, we studied formation of nanostructured TiB2-Cu composites under shock wave conditions. We investigated the influence of preliminary mechanical activation (MA) of Ti-B-Cu powder mixtures on the peculiarities of the reaction between Ti and B under shock wave. In the MA-ed mixture the reaction proceeded completely while in the nonactivated mixture the reagents remained along with the product – titanium diboride. The size of titanium diboride particles in the central part of the compact was 100-300 nm. This research shows that shock wave synthesis in mechanically activated powder mixtures with simultaneous compaction of the composite is a promising way to materials with submicron and nanostructures.