Papers by Author: Oleg Smorygo

Abstract: Zirconia-alumina ceramic foam scaffolds with a nanocrystalline HAP coating were used for the preparation of integrated motile orbital implants. This study demonstrated that open-cell ceramic foams with enhanced strength-to-density ratio are quite suitable as biocompatible materials for the manufacture of orbital implants for post-enucleation syndrome treatment. In-vivo studies demonstrated that the application of a nanocrystallyne (not sintered) HAP coating facilitated the formation of dense fibrous capsule around the implant as well as the fast tissue ingrowth into the implant’s internal space. Orbital implants with the optimized pore size and HAP content were implanted to the animal’s eye cavity with their fixation to the extraocular muscles, and their motility was ensured.

Abstract: Gradient permeable metallic substrate material consisting of two layers of NiAl alloy was developed for the SOFC design. The open-cell foam layer (thickness 1-2 mm, cell density 60 ppi) provides the structure robustness, while a thin (100-200 μm) mesoporous layer facilitates supporting functional layers. Cathode layers (LSM, LSFN and their nanocomposites with GDC or YSZ) and anode layers (NiO/YSZ, NiO/YSZ +Ru/Ln-Sr-Mn-Cr-O nanocomposite catalyst) were deposited by slip casting, electrophoretic deposition or air brushing. Thin (5-10 μm) YSZ layer was deposited by MO CVD. Power density up to 550 mW/cm2 at 700oC was obtained on button-size cells using wet H2-air feeds.

Abstract: Metallic and ceramic foam catalyst supports and catalysts were manufactured. Comparative studies of the foam-structure catalyst supports and straight-channel catalysts supports were performed. Affect of the catalyst support pore structure upon the catalyst operational performance was analyzed.