Papers by Author: Rudi Cloots

Abstract: This paper is focused on the preparation and characterization of different lamellar silica prepared by liquid crystal templating and silanisation. The initial template can be removed and replaced in the interlamellar spaces by different types of silane, being covalently grafted to the solid by reaction with the surface silanols. The lamellar stacking periodicity remains after this modification. The surfactant extraction can lead in significant grafting of isopropanol if the solid is simply refluxed in isopropanol, which have the effect of preserving the periodicity of the lamellar stacking. The surfactant extraction in an Soxhlet equipment avoid this reaction, with the effect of platelets organization collapsing. The lamellar silica studied exhibit great specific surface and combination of meso and microporosity, making them interesting materials for nanocomposite or catalysis applications.

Abstract: Thin hexagonal barium hexaferrite particles synthesized using the microemulsion technique were studied. A water-in-oil reverse microemulsion system with cetyltrimethylammonium bromide (CTAB) as a cationic surfactant, n-butanol as a co-surfactant, n-hexanol as a continuous oil phase, and an aqueous phase were used. The microstructural and magnetic properties were investigated. The particles obtained were mono-domain with average particle size 280 nm. The magnetic properties of the powder were investigated at 4.2 K and at room temperature. The saturation magnetization was 48.86 emu/g and the coercivity, 2.4 x 105 A/m at room temperature. The anisotropy field Ha and magneto-crystalline anisotropy K1 were 1.4 x 106 A/m and 2.37 x 105 J/m3, respectively.

Abstract: Barium hexaferrite (BaFe12O19) powders of particle size of 130 and 180 nm were synthesized by a single microemulsion technique. The influence of the concentration of Ba2+ and Fe3+ metallic ions in the aqueous phase in the microemulsion system on the particle size distribution, crystallinity and magnetic properties of BaFe12O19 was studied. The coercive force and saturation magnetization of the sample obtained at a lower concentration of metallic cations in the aqueous phase were higher than those of the sample obtained at higher concentration.

Abstract: YBa2Cu3O7-δ coatings were deposited by electrophoretic deposition (EPD) onto Ni substrates. Particles of different sizes and shapes were used in order to study the influence of the powder microstructure on the film density. Texturation of the thick films was induced by application of a magnetic field during the electrophoretic deposition. X-ray diffraction analysis has clearly shown preferred c-axis alignment of the YBa2Cu3O7-δ films along the direction normal to the substrate surface. Scanning electron microscopy and optical polarised light microscopy were used to characterise the microstructure of the coatings, revealing a nonrandom platelets organisation.