Abstract: In the present work, we report on the effects of the implantation temperature on the formation of bubbles and extended defects in Ne+-implanted Si(001) substrates. The implantations were performed at 50 keV to a fluence of 5x1016 cm-2, for distinct implantation temperatures within the 250°C≤Ti≤800°C interval. The samples are investigated using a combination of cross-sectional and plan-view Transmission Electron Microscopy (TEM) observations and Grazing Incidence Small-Angle X-ray Scattering (GISAXS)measurements. In comparison with similar He implants, we demonstrate that the Ne implants can lead to the formation of a much denser bubble system.

Abstract: In this paper we present a detailed study in which the formation, by heavy ion impact, and thermal recrystallisation of individual amorphous zones have been studied using in-situ transmission electron microscopy. In agreement with previous work, we observe a reduction in the total volume of amorphous material contained within the amorphous zones following thermal annealing over a wide range of temperatures. When the evolution of the individual amorphous zones is followed, those with similar starting sizes are observed to recrystallise over a range of temperatures from 70 °C to 500 °C. The temperature at which an amorphous zone fully recrystallises does not appear to be correlated with initial size. In addition, zones are occasionally observed to increase in size temporarily on some isochronal annealing steps. Furthermore, observations during a ramp anneal show that many zones recrystallise in a stepwise manner separated by periods of stability. These phenomenon are discussed in terms of the I-V pair.