Abstract: Thermal behaviors of EAF dust, water-washed EAF dust, and EAF dust/heavy clay mixtures with wet mixing process were characterized by TG/ DTA analysis. The ionic concentrations of some metal ions and anions in the supernatant from water-washing process were evaluated by ICP and IC analysis. Weight loss of water-washed EAF dust above the temperature range of 1000°C was significantly decreased because of the washing effect of chloride and sulfate compounds. The variation of volatile ZnO and PbO contents were not detected in 20wt% D dust-80wt% clay sample. The wet mixing process not only enhanced the homogeneous mixing of EAF dust and clay particles, but also reduced the volatilization of heavy metals(Zn, Pb, etc.) at the high temperature range.

Abstract: Brick samples were prepared through vitrification process with two different kinds of EAF dust. Leaching concentrations of various metal ions and anions for the bricks(20wt% EAF dust-80wt% clay) were evaluated by ICP and IC analysis. The results of leaching test showed that the concentration of ions leached from bricks were proportional to the square root of time and saturated with leaching time. The saturated concentrations of alkali and alkali-earth metal ions were 0.1-250ppm; on the other hand, the heavy metal ions were 0-0.084ppm. The efflorescence mechanism of EAF dust-clay bricks was studied by quantitative analysis for the effects of various metal ions and anions. Efflorescence formed on the brick surfaces which were immersed in DI water and dried slowly in the air were characterized by SEM, EDS and XRD. The results of EDS and XRD showed that the main component of the efflorescence was water soluble Na₂SO₄ .