Papers by Author: Sandra G. Schneider

Abstract: Many materials with different surfaces have been developed for dental and orthopedics implants. Among the various materials for implants, titanium and bioactive ones such as calcium phosphates and hydroxyapatite, are widely used clinically. When these materials are inserted into bone several biological reactions occur. Thes processes can be associated with surface properties (topography, roughness and surface energy). In this work, ingots were obtained from titanium and molybdenum by using an arc-melting furnace. They were submitted to heat treatment at 1100°C for one hour, cooled in water and cold worked by swaging. Titanium nanotubes were fabricated on the surface of Ti-7,5Mo alloy by anodization, and then treated with NaOH solution to make them bioactive, to induce growth of calcium phosphate in a simulated body fluid. . It is shown that the presence of titanium nanotubes induces the growth of a sodium titanate nanolayer. During the subsequent in-vitro immersion in a simulated body fluid, the sodium titanate nanolayer induced the nucleation and growth of nano-dimensioned calcium phosphate. These titanium nanotubes can be useful as a well-adhered bioactive surface layer on Ti implant metals for orthopedic and dental implants.

Abstract: Measurements of anelastic relaxation (internal friction and frequency) as a function of temperature were carried out in samples of Ti-13Nb-13Zr using two experimental apparatus: Flexural Vibration of the first tone of samples in Acoustic Elastometer System (Vibran Technology®) operating in a kilohertz bandwidth, and Torsional Vibration of the samples in Kê-type Torsion Pendulum operating in a hertz bandwidth. Experimental spectra of anelastic relaxation were determined in the temperature range from 300 K to 450 K for a heating rate of 1K/min under pressure of 10-5 Torr, in both apparatus. The results show a relaxation structure strongly dependent on the microstructure of the material. The dynamical elastic modulus (E) of Ti-13Nb-13Zr alloy can be determined by flexural vibrations by frequency (f) measurements (f  E1/2). The anelastic relaxation spectrum of Ti-13Nb-13Zr alloy was a function of temperature obtained by torsional vibrations, not revealing the presence of interstitial solutes in solid solution in the temperature range of measurements.

Abstract: Recent studies have been done to achieve biomedical alloys containing non-toxic elements and presenting low elastic moduli. It has been reported that Ti-Nb-Zr alloys rich in beta phase, especially Ti-13Nb-13Zr, have potential characteristics for substituting conventional materials such as Ti-6Al-4V, stainless steel and Co alloys. The aim of this work is to study the internal friction (IF) of Ti-13Nb-13Zr (TNZ) alloy due to the importance of the absorption impacts in orthopedic applications. The internal friction of this alloy produced by arc melting was measured using an inverted torsion pendulum with the free decay method. The measurements were performed from 77 to 700 K with heating rate of 1 K/min, in a vacuum better than 10-5 mBar. The results show a relaxation structure at high temperature strongly dependent on microstructure of the material. Qualitative discussions are presented for the experimental results, and the possibility of using the TNZ as a high damping material is briefly mentioned.