Papers by Author: Sebastjan Žagar

Abstract: The paper deals with the effect of different shot peening (SP) treatment conditions on the ENAW 7075-T651 aluminium alloy. Suitable residual stress profile increases the applicability and life cycle of mechanical parts, treated by shot peening. The objective of the research was to establish the optimal parameters of the shot peening treatment of the aluminium alloy in different precipitation hardened states with regard to residual stress profiles in dynamic loading. Main deformations and main residual stresses were calculated on the basis of electrical resistance. The resulting residual stress profiles reveal that stresses throughout the thin surface layer of all shot peened specimens are of compressive nature. The differences can be observed in the depth of shot peening and the profile of compressive residual stresses. Under all treatment conditions, the obtained maximum value of compressive residual stress ranges between -200 MPa and -300 MPa at a depth between 250 μm and 300 μm. Comparison of different temperature-hardened aluminium alloys shows that changes in the Almen intensity values have greater effect than coverage in the depth and profile of compressive residual stresses. Positive stress ratio of R=0.1 was selected. Wöhler curves were determined in the areas of maximum bending loads between 30 - 65 % of material's tensile strength, measured at thinner cross-sections of individual specimens. The results of material fatigue testing differ from the level of shot peening on the surface layer.

Abstract: In the paper two aluminium alloys, i.e. 6082 and 7075, which were cold hardened by shot peening under different conditions, are treated. Surface hardening was carried out with S170 steel shot of the same diameter, particle hardness being 56 HRC. Other conditions were the operating pressure, mass flow, which provide different Almen intensities. The hardened layer was described by surface integrity. Macroscopic and microscopic analyses consisted in analyses of hardened profiles of hardness, and residual stresses in the thin surface layer. Research results indicated that there were significant differences among the characteristics chosen to describe surface integrity and that they had an important influence on the final condition of the surface layer. With too severe settings of the peening parameters, the surface properties got worse because of damages, which resulted in crack initiation and growth of the existing cracks.