Papers by Author: Sergey V. Veselov

Abstract: The aim of the work was to clad Ti-Ta-Nb coating on a substrate of pure titanium. Cladding was carried out by non-vacuum electron-beam treatment. As a result a good quality coating thickness of about 2 mm was obtained. Microstructural and microhardness tests were conducted. Dendritic structure and the borders of the former grains of β-phase were revealed. At the microlevel, the coating has a martensitic structure. The average hardness of coating is about 4000 MPa.

Abstract: Structure, microhardness and fracture features of coatings produced by atmospheric electron-beam cladding of amorphous boron were investigated. The coatings were produced by cladding of one, two and three layers of powder. Produced coatings thickness is 550, 750 and 900 μm respectively. The peak level of microhardness is 14000…16000 MPa. By the means of XRD analysis it is stated that the main phases of strengthened layers are FeB and Fe₂B borides and eutectic (α-Fe + Fe₂B). The coatings after one layer cladding have non-uniform structure with microvolumes having lack of borides. Three-layered coatings are noted for their high brittleness. The best properties are presented by two-layer coatings.