Papers by Author: Shunsuke Hirukawa

Abstract: Proton conducting ZrO2－yP2O5 (y = 1.0, 1.2, 1.4. 1.6, 1.8) electrolytes based on a shell-core structure were synthesized with diammonium hydrogen phosphate by a solid state reaction, and their conductivities were investigated by ac-impedance spectroscopy. Among the ZrO2-yP2O5 compositions, ZrO2－1.6P2O5 showed the highest proton conductivity of 0.13 Scm-1 at 250°C. The conductivity increased with increasing P2O5 molar ratio and were significantly influenced by heat-treatments in the preparation process. Polytetraflouroethylene (PTFE) was also mixed into these electrolytes in order to improve the mechanical strength and long term durability.

Abstract: Shell-core type TiP2O7-based electrolytes were synthesized by a low-temperature sol-gel method, and their conductivities were investigated by ac-impedance spectroscopy. The samples heat-treated at 500°C showed higher proton conductivities of 3.8 × 10-2 - 1 × 10-2 Scm-1 at intermediate temperatures (100 - 300°C). The conductivity decreased by reheat-treatments at 600°C and 700°C due to a decrease in the amount of the conductive amorphous shells. However, the mechanical strength of the sample pellet significantly increased by the reheat-treatment. The sample reheat-treated at 600°C kept high conductivities of 8.8 × 10-3 - 1 × 10-3 Scm-1 in a range of 100°C - 300°C.