Papers by Author: Stefan Riekehr

Abstract: The present work investigates the effects of laser beam power, focus position and advance speed on the geometry, microstructure and mechanical properties of fiber laser beam welded Ti-6Al-2Sn-4Zr-2Mo (denoted as Ti-6242) butt joints used for high temperature applications. Detailed microstructural and mechanical studies were performed on welds produced using optimized parameters (a laser beam power of 5 kW, a focus position of 0.0 mm and an advance speed of 6.2 m/min). The Ti-6242 base material is characterized by a globular (α+β) microstructure. The heat input during laser beam welding led to the formation of a martensitic α’-phase fusion zone. The heat affected zone consisted of globular grains and acicular crystallites. These local transformations were connected with a change in the micro-texture, average grain size and β-phase content. Furthermore, the microhardness increased from 330 HV 0.3 to 450 HV 0.3 due to the martensitic transformation. The mechanical behavior of the laser beam welded Ti-6242 butt joint loaded in tension was determined by the properties of the Ti-6242 base material. The local increase in hardness provided a shielding effect that protected the Ti-6242 butt joint against mechanical damage.

Abstract: A hollow rectangular profile, as an example of a typical structural component made of magnesium alloy sheets has been built, tested and evaluated in order to assess its behaviour during axial crushing. The profiles were joined from plane sheets of AZ31 and ZE10, respectively, by laser beam welding and were then tested in compression. Numerical simulations have been conducted to understand the complex interplay between hardening characteristics of the materials under investigation, profile cross-section variation and energy absorption. The results from the compression testing of the profiles show that the welds are not the source of damage initiation and failure. The performance of the magnesium profiles in terms of dissipated specific energy is confirmed for small and intermediate displacements to be comparable to that of aluminium profiles. For large displacements, however, the shear-type failure mode of magnesium causes a sharp drop of the crushing force and thus limits the energy absorption. These findings demonstrate the requirement for an alloy and wrought magnesium process development specifically for crash applications which aims at progressive hardening along with high ductility for improving the bending and shear behaviour.

Abstract: The effect of different welding sequences between a 4.5 mm thick AA 6156 T6 base plate and a 2 mm thick AA 6013 T6 clip – resembling a skin-clip joint of an airframe – using a 3.3 kW Nd:YAG laser is investigated. Under cyclic loading the breakdown of such T-joints happens at one end of the clip, which is due to local residual stress concentrations. Recent measurements indicated that tensile stresses could be lower at the run-in than at the run-out locations. For a deeper investigation of this effect sheets with different welding sequences were produced. One welding sequence was made with two starting points in the centre, and a second with starting points at the clip ends. Temperature measurements were made using thermocouples to verify the heat conditions for a finite element simulation of the welding process, which is used for predictions of the residual stress distribution. Actual values of the residual stress fields were determined by neutron diffraction. The influences of the welding sequence on the measured temperatures and the residual stresses are discussed.

Abstract: Microstructure, hardness and residual stresses of the laser beam overlap welds between AZ31B sheets and AZ31, AZ61 and AZ80 extruded profiles are investigated using microscopy and X-ray diffraction. The result of the investigations reveal that weld microstructure, the size of the HAZ, precipitate density and the maximum compressive residual stress values depend strongly on the Al content of the weld zone of two Mg-alloys.

Abstract: Dissimilar welded components joined with any kind of welding technologies gain an increasing interest due to significant improvements in engineering structures by using new materials (alloys) or new materials combinations. The present paper deals with laser welding of Al5083-H111 and Al6013-T6 and the characterization of the crystallographic texture. Fine grained Al5083 was joined with coarser grained Al6013.Whereas, Al6013 is strongly oriented dominated by a strong cube component and a much lower Goss component, the finer grained Al5083 shows a week deformation texture. The welding seam itself has a moderate cube texture with a minor <100> fiber texture in welding direction. A small texture variation about the texture strength and the volume fraction of the fiber component was observed along the weld. Results were obtained by neutron, hard X-ray and electron diffraction.