Abstract: Lotus-type porous aluminum with cylindrical pores oriented in one direction was deformed by Equal Channel Angular Extrusion (ECAE) through a 150° die with sequential 180° rotations, and the pore morphology and Vickers hardness after the extrusion were investigated. The Vickers hardness increases with increasing number of passes in the extrusions both parallel and perpendicular to the pore direction, accompanied by the decrease of porosity. The densification occurs more easily in the perpendicular extrusions than in the parallel extrusions, and the large deformation by the densification gives rise to the large increase in the Vickers hardness for the perpendicular extrusions.

Abstract: Porous Al-5mass%Ti alloys were fabricated using a continuous casting technique in a hydrogen atmosphere, and the effects of transfer velocity (V) and the peritectic solidification process on the pore morphology and matrix microstructure were examined. In the case of V = 0.5 mm/min, columnar microstructure and directional pores grow along the transfer direction. The Al3Ti phases are formed in localized regions of matrix part, and however, they do not suppress the growth of directional pores in the other regions. In the case of 5.0 mm/min, because needle-like Al3Ti phases grow along the transfer direction, directional pores can grow between them. On the other hand, in the case of 10.0 mm/min, spherical pores surrounded by equiaxed peritectic microstructure and homogeneously distributed Al3Ti phases are formed, because the primary α -Al and Al3Ti phases probably prevent the growth of directional pores.