Papers by Author: Tae Ryong Kim

Abstract: Inconel alloy such as alloy 600 and alloy 690 is widely used as the steam generator tube materials in the nuclear power plants. The impact fretting wear tests were performed to investigate wear mechanism between tube alloy and 409 stainless steel tube support plates in the simulated steam generator operating conditions, pressure of 15MPa, high temperature water of 290°C and low dissolved oxygen(<10 ppb). From investigation of wear test specimens by the SEM and EDS analysis, hammer imprint, which is known to be an actual damaged wear pattern, has been observed on the worn surface, and fretting wear mechanism was investigated. Wear progression of impact-fretting wear also has been examined. It was observed that titanium rich phase contributes to the formation of voids and cracks in sub-layer of fretting wear damage by impact fretting wear.

Abstract: A statistical assessment model for structural integrity of steam generator tubes with axial cracks at the top of the tubesheet was proposed using Monte Carlo method. In the model, a method for estimating the number of "real cracks" from in-situ inspection (ISI) data was used. Based on the estimated "real cracks", the number of newly detected cracks and growth of cracks during arbitrary operating period were simulated using the Monte Carlo method. The flaw growth rate used in the simulation was statistically calculated from the periodic in-service non-destructive inspection data. The number of cracks, the probabilistic distribution of crack sizes at the end of next operating interval and the probability of burst during operation were calculated from numerously repeated simulations using the proposed model.