Papers by Author: Tetsuhide Shimizu

Abstract: Grain refinement processing by severe deformation, combined equal-channel angular extrusion (ECAE) processing and conventional tube extrusion, is applied to AZ31 magnesium alloy. By a combination of ECAE processing and tube extrusion, a fabricated tube, with outer and inner diameters of 2 mm and 1 mm, respectively, has fine, homogeneous, and equiaxed grain structure with an average grain size of 1.5m. Tensile test results indicate that the fine-grained tubes exhibited a superplasticity potential m value of 0.55.The maximum elongation (688%) is obtained at a temperature of 673K. Furthermore, the tubes fabricated by combined ECAE/extrusion process is applied to dieless drawing process without using any tool and die.As a result, dieless drawing limit is enhanced due to high m value achieved by combined ECAE/Extrusion process. From these results, the effectiveness of new grain refinement processing for fabricating fine-grained tubes and its application for dieless drawing process to fabricate the fine tubes was demonstrated experimentally.

Abstract: This study focuses on the surface deformation of thin metal foils caused by friction. To clarify the effect of the relative ratio of surface plastic region to the foil thickness on global deformation behavior, strip drawing tests for ultra thin metal foil with 20μm and 100μm thickness were conducted As a result, different surface deformation and elongation behavior under the same friction condition were observed in different thicknesses. Aided by finite element analysis of the friction test, the contribution of the deformation caused by friction to the foil elongation was investigated and the importance of the friction on material deformation in metal foil forming was demonstrated.