Abstract: The load transfer among ferrite orientations and between ferrite and martensite was analysed in DP 600 steel by means of neutron diffraction during in situ tensile tests on the multiple pulse overlap time-of-flight strain scanner POLDI. The material had 0.07 wt% C and a martensite volume fraction of 15%. In situ tests were done in “Young” as well as in “Poisson setup”. The martensite phase could not be probed due to its low tetragonality. The curves of the lattice plane strains as a function of the externally applied macroscopic stress reveal (1) plastic relaxations of transformation and intergranular stresses in the compliant <100> oriented grains, and (2) a second inflection point in the fully plastic part indicating the onset of plastic deformation of the hard phase.

Abstract: Seamless tubes are used for many applications, e.g. in heating, transport gases and fluids, evaporators as well as medical use and as intermediate products for hydroforming and various mechanical applications, where the final dimensions normally are given by some cold drawing steps. The first process step – piercing of the billet, for example by extrusion or 3-roll-milling - typically results in ovality and eccentricity in the tube causing non-symmetric material flow during the cold drawing process, i.e. inhomogeneous deformation. Because of this non-axisymmetric deformation and of deviations over tube length caused by moving tools, this process step generates residual stresses. To understand the interconnections between the geometrical changes in the tubes and the residual stresses, the residual strains in a copper tube had been measured by neutron diffraction.