Papers by Author: Wei Yong Yang

Abstract: A water-soluble CdTe QDs capped by 3-Mercaptopropionic acid (MPA) were synthesized. The results confirmed that the grain size of the QDs was controlled by changing the reflux time of precursor solution and that the QDs possessed obviously quantum size effect. The results showed that a depletion layer CdTe_1-xS_x (0£x≤1) formed in between CdTe nanoparticle and ligand MPA. It is believed that two heterojunction-like structures possess quite distinct surface photovoltaic characteristic excited between the core-CdTe and the shell-CdS, and between CdTe/CdS and the ligand MPA, respectively, according to the EFISPS results of the MPA-capped CdTe QDs.

Abstract: The Macroporous Nanocrystalline TiO₂ Thin Film Was Prepared by Dipping-Coating Method. Polystyrene (PS) Microspheres Template Was Used as Pore-Forming Assistant and TiO₂ Sol Was Used as Precursor. the Photoelectric Characteristics of the Samples Were Studied Using Surface Photovoltage (SPV) and Photoacoustic (PA) Techniques. the Presence of a Small Amount of Residual Template Damages the Integrity of the Porous TiO₂ Film with Inverse Opal Structure, and TiO₂ May Be Restricted in Certain Application Fields as Photonic Crystals. a Small Amount of Residual Template Changes the Surface Photovoltaic Properties of the Porous TiO₂ Film, Resulting Mainly in the Broadened Scope and the Increased Intensity of SPV Response.