Papers by Author: Xiao Na Li

Abstract: The aim of this investigation is to study the effect of SnO coatings on the bond strength between titanium and porcelain. The coatings were produced by sol-gel method and heat-treatment at 300°C. Once the coatings have been formed on the titanium substrates, self-made porcelain was fused. The specimens with pre-oxidation before porcelain fused were set as control group. It was shown SnO gel formed completely at 300°C and was composed by SnO and SnO2 in the form of a uniform film. The bond strength between titanium and porcelain of the specimens with SnO coatings was greater than those in control group statistically, which might prove that the coatings reduced the oxidation of titanium surface in the porcelain fusing progress. EDS result showed almost all fractures between titanium and porcelain occurred at the oxide layer. Si and Sn might attend the reaction at interface. It was concluded that the SnO coatings produced in this study can improved the titanium-porcelain bond strength.

Abstract: Partially sintered zirconia ceramics (PSZCs) for dental uses were prepared from zirconia nanopowder via isostatic pressing and partially sintering. The open porosities, pore diameters, grain sizes and mechanical properties of the ceramics with different densities were studied. The results show that the pores formed in the PSZCs are all open pores, with a diameter distribution of 60nm~130nm and a grain size distribution of 120~170nm. The machinability becomes worse when the density of PSZC is higher than 75% of the theoretical density, so a ceramic named PSZC-70% with density of 70%TD was selected as the target material. Its bending strength is 168 MPa and fracture toughness is 1.8 MPa·m1/2. A dental restoration framework can be obtained via machining the PSZC-70% on a dental CAD/CAM system.