Abstract: Cored wires and high velocity arc spraying technique (HVAS) were used to produce high Mg content Zn-Al-Mg alloy coatings on low carbon steel substrates. The microstructures, mechanical properties and electrochemical corrosion behaviors of the Zn-Al-Mg coatings were investigated comparing with Zn and Zn-Al alloy coatings. And the electrochemical corrosion mechanisms of the coatings were discussed. The coatings show a typical aspect of layered thermal sprayed material structure. Chemical analysis of the coating indicated the composition to be Zn-14.9Al-5.9Mg-3.0O (wt.%). The main phases in the coatings are Zn, Mg2Zn11, Al12Mg17 and MgAl2O4, together with a little Al2O3 and ZnO. The corrosion potential of Zn-Al and Zn-Al-Mg coatings decreased a little and then increased towards the noble potential. With addition of Mg, the corrosion products accumulated to form stable passive film can block off the pores in the Zn-Al-Mg coating, and thus may prevent attack on the underlying steel substrate. The Zn-Al-Mg coatings show higher electrochemical corrosion resistance in salt solution than Zn-Al coatings.

Abstract: Cored wires and high velocity arc spraying (HVAS) technologies have been applied to produce Zn-Al-Mg-RE coating on A3 steels. The durability of coating in terms of corrosion resistance is the focus of this paper. The detailed degradation mechanism has been investigated using electrochemical-monitoring techniques supported by precise pre-test and post-test microscopical examination using Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). Zn-Al-Mg-RE coating shows a typical aspect of layered heterogeneous structure, the existing of ZnAl2O4 and MgAl2O4 implies the good anti-corrosion feature. The polarization curves showed that Zn-Al-Mg-RE coating exhibits passive behavior at 0.5h and 16h immersion, but at 600h, it begins to dissolute. In contrast, the anti-corrosion performance isn’t cut down. The corrosion potential moves to the noble direction step by step, along with the current density drops gradually. After corrosion, it has been observed that the coating surface is jointed by flaky lamellar products and dense without obvious defects and pores. It is postulated that with the addition of RE, the porosity of the coating is reduced, meanwhile, the stability of the products layer can reinforce the self-sealing effect of the coating distinctively.