Abstract: In this research, the urea-formaldehyde prepolymer and multilayer hot-press drying was used to obtain modified wood. The timbers were compressed and dried by the multilayer hot-press drying kiln. The combination of chemical modification and hot-press drying can improve the drying rate, which can also enhanced the physical and mechanical properties. Based on the findings, the basic density of modified wood improved 25.2 %, the bending strength and the bend elastic modulus improved 15.6 % and 25.0 % respectively. The dimensional stability of the treatment appeared to be slightly higher than that of untreated samples under the same conditions for processing temperatures and times. The improving dimensional stability of wood mainly was attributed to the prepolymer that changes wood cell wall components such as the degradation of the hemicelluloses and cellulose during hot-press drying treatment. The XRD results indicated that the degree of crystallinity increased to 35.45 %from 31.25 %. The TGA results show that the degradation of the samples can be divided into two step, both of the maximum weight loss velocity temperature of the two step increased to 266 °C, 355 °C from 244 °C and 341 °C.

Abstract: In this research, the chemical and multilayer hot-press drying was used to modify poplar wood. The timbers were compressed and dried in the multilayer hot-press drying kiln. The combination of chemical modification and hot-press drying can improve the mechanical properties. The influence of chemical and hot-press drying on the compressive strength parallel to grain, the bending strength, the density, the water absorbent and the crystallinity of poplar wood have been investigated in this study. The chemical treated conditions close to real technological regimes selected. The samples were impregnated with three conditions. The samples were dried in a hot-press drying kiln for 130hrs. It was showed that the urea carbamate and hot-press drying treatment increase the properties. The density and mechanical properties increased with increasing urea carbamate, while the water absorption decreased. The crystallinity is 37.03%, 37.11%, 37.78%, separately, compared with the natural wood of 35.09%. The TAG showed the thermal stability increased.