Papers by Author: Yi Han Liu

Abstract: The aim of this study were to compare the color value of four kinds of dental all-ceramic cores (IPS e.max Press,Zenostar,Lava Zirconia and Upcera Zirconia) on three different post-core materials.All-ceramic core materials were made into samples at the diameter of 10mm and the thickness of 0.50.02mm.Their color value on the post-core material of noble metal,Co-Cr alloy and resin were respectively determined with chromatism instrument.It was showed that the color value of four all-ceramic cores were statistically different.IPS e.max Press was most obviously affected by post-core materials,while Upcera Zirconia the weakest.Lava Zirconia and Zenostar were influenced to a certain degree.In conclusion,non-mental post-core was preferable for IPS e.max Press,Upcera Zirconia was fit for any post-core materials.

Abstract: The purpose of this study was to compare the transmittance of four dental all-ceramic core materials at clinical recommendation thickness.Specimens with 10mm in diameter and 0.50.01mm in thickness,including IPS e.max Press,Zenostar Zirconia,Lava Zirconia and Upcera Zirconia,were fabricated.The transmittance of specimens were measured with PR2650 spectrophotometer and measurements were analysed statistically with SPSS13.0.Experimental results showed that they had significantly different transmittance.There was a decreasing order,IPS e.max Press Lava Zirconia Zenostar Zirconia Upcera Zirconia,which were 6.1136.750 for IPS e.max,1.6042.135 for Lava Zirconia,1.5782.117 for Zenostar Zirconia and 0.9951.265 for Upcera Zirconia.

Abstract: The present paper probes into the effect of background color of different post-core materials on the core materials of In-Ceram AL2 Electroformed Alumina, Z21 Electroformed Zirconia, Cercon base color Zirconia, and Cercon base Zirconia. The spectrocolorimeter was used to measure colorimetric values of all groups of samples against the background of noble metal, nickel-chromium alloy, silver amalgam and resin, and to calculate the color difference among the groups. The result showed that the color difference of Cercon base color Zirconia viewed against different backgrounds was identifiable by human eyes (ΔE > 1.5). In contrast, the color differences of In-Ceram AL2 Electroformed Alumina, Z21 Electroformed Zirconia and Cercon base Zirconia viewed against different backgrounds were unidentifiable by human eyes (ΔE < 1.5). Based on this, it can be stated that Cercon base color Zirconia is significantly affected by background color. Thus, proper method to shelter the background color should be adopted. In addition, AL2 Electroformed Alumina, Z21 Electroformed Zirconia, and Cercon base color Zirconia are less influenced by the background color, thus it is not necessary to cover the background color.

Abstract: The spectral transmittance of six kinds of Vita In-Ceram and Cercon all-ceramic core materials after veneering ceramic was determined. Based on the production method recommended by the manufacturer, specimens of the same thickness are made. PERKIN ELMER Spectrophotometer is adopted to measure the spectral transmittance of In-Ceram AL2 slip-casting glass/alumina composite, AL2 electroformed alumina, Z21 slip-casting glass/zirconia composite, Z21 electroformed zirconia, Cercon base color zirconia and Cercon base zirconia all-ceramic core materials, after veneering ceramic. The results show that, after veneering ceramic, Cercon base Zirconia has the highest spectral transmittance, followed by AL2 Electroformed Alumina and Z21 Electroformed Zirconia, whereas the transmittance of Z21 slip-casting Glass/Zirconia composite has the lowest. Statistical data show that, among the groups, In-Ceram slip-casting Glass/Alumina composite (AL2), Electroformed Alumina (AL2), Cercon base color Zirconia and Cercon base Zirconia have significant differences between every group. On the other hand, there is no significant difference between In-Ceram slip-casting Glass/Zirconia composite (Z21) and Electroformed Zirconia (Z21). Therefore, we should choose all-ceramic restoration materials based on the spectral transmittance of all-ceramic core materials after veneering ceramic and transparency of the remaining natural teeth of patients.